| Properties Applicable for 1.5 mm thick material as per) | IS 2712/1998 |
| Density) | 1.7-2.2gm/cm3 |
| Tensile Strenght) | >24.0 Mpa. |
| Compressibility) | 6-14% |
| Recovery) | >40% |
| Stress Relaxation) | 23.0 Mpa. |
| Ignition Loss) | <28% |
| FLUID ABSORPTION) | --- |
| Water) | |
| Mass Increase) | |
| In ASTM OIL No.3) | (In refrigearting Oil) |
| Thickness Increase) | <5% |
| Mass Increase) | <5% |
| In FUEL B) | |
| Thickness Increase) | |
| Mass Increase) | |
| In IRM 903) | |
| Thickness Increase) | |
| Mass Increase) | |
| Sulphuric Acid (96%)) | |
| Thickness Increase) | |
| Tensile Strength Decrease) | |
| Nitric Acid (95%)) | |
| Thickness Increase) | |
| Tensile Strength Decrease) | |
| Peak Temp oc) | -80 to +450 |
| max. Operating Pressure Kg/cm2) | 100 |
Ferolit 'K'
Ferolit 'K'
-For high stress conditions.
-For chlorinated hydro carbon, Ammonia & refrigerating oils
Specification Compliance
IS 2712/1998 Grade W/3